Medical Titanium, Round Disc for Dentistry, CP Titanium, Alloyed titanium, Grade 1, Ti6Al4V Eli, ISO5832-2/3
Medical Titanium Round Disc for Dentistry
Grades: Grade 1, Grade 2，Ti6Al4V ELI
Pure Ti Gr Medical: Pure Titanium disc... for unparalleled biocompatibility.
Composition (in % by mass): Ti 99.5
Alloyed Ti Gr Medical: Titanium disc with increased mechanical properties.
Composition (in % by mass): Ti 89.5; Al 6.0; V 4.0; Fe < 1.0; O < 1.0
Availability:
Type 1 (Ø 98mm discs) :
- WITH step : 12,14 and 18mm.
- WITHOUT step : 10, 12, 14 and 18mm.
Type 2 (20g, 25g, 30g, 35g, 40g)
Surface: Polished
Status: Rolled & Annealed
Features:
- ASTM F67, ASTM F136 approved
- Biocompatible
- Light weight and easy to mill
- Corrosion-resistant
Indications :
Dental restoratoins including crowns and bridges, copings, abutments and implant bars.
Production Capability:
30 Metric Tons/month
Packing:
Standard export plywood case
Delivery Time:
5-15 days
Shipping:
By International Express(TNT, FEDEX, DHL, UPS, etc.), By Air, By Sea
Titanium Products for Medical Use.pdf
Medical Titanium Round Disc for Dentistry
Medical Titanium, Round Disc for Dentistry, CP Titanium, Alloyed titanium, Grade 1, Ti6Al4V Eli, ISO5832-2/3
ASTM F67 Unalloyed Titanium, for Surgical Implant Applications (UNS R50250, UNS R50400, UNS R50550, UNS R50700)
Medical CP Titanium Chemical Composition:
| Element | CompositionA, % (mass/mass) | |||
| Grade 1 UNS R50250 | Grade 2 UNS R50400 | Grade 3 UNS R50550 | Grade 4 UNS R50700 | |
| Nitrogen, max | 0.03 | 0.03 | 0.05 | 0.05 |
| Carbon, max | 0.08 | 0.08 | 0.08 | 0.08 |
| Hydrogen, max | 0.015 | 0.015 | 0.015 | 0.015 |
| Iron, max | 0.20 | 0.30 | 0.30 | 0.50 |
| Oxygen, max | 0.18 | 0.25 | 0.35 | 0.40 |
| Titanium | balance | balance | balance | balance |
Medical CP Titanium Mechanical Properties:
| Grade | Tensile Strength(min) | Yeild Strength(min) | Elongation in 4D, min, % | Reduction of Area, min, % | ||
| ksi | MPa | ksi | MPa | |||
| Grade 1 | 35 | 240 | 20 | 138 | 24 | 30 |
| Grade2 | 50 | 345 | 40 | 275 | 20 | 30 |
| Grade 3 | 65 | 450 | 55 | 380 | 18 | 30 |
| Grade 4 | 80 | 550 | 70 | 483 | 15 | 25 |
ASTM F136 Titanium-6Aluminum-4Vanadium ELI (Extra Low Interstitial) Alloy for Surgical Implant Applications (UNS R56401)
Medical Alloyed Titanium Chemical Compositions:
| Element | Composition, % | |||||||
| Nitrogen, max | 0.05 | |||||||
| Carbon, max | 0.08 | |||||||
| Hydrogen, max | 0.012 | |||||||
| Iron, max | 0.25 | |||||||
| Oxygen, max | 0.13 | |||||||
| Aluminum | 5.5–6.50 | |||||||
| Vanadium | 3.5–4.5 | |||||||
| Titanium | balance | |||||||
Medical Alloyed Titanium Mechanical Properties:
| Nominal diameter or distance between parallel sides, in (mm) | Tensile strength min,psi (MPa) | Yield Strength (0.2 % offset) min, psi (MPa) | Elongation in 4D or 4W min, % | Reduction of area min, % | ||||
| L | LT | ST | L | LT | ST | |||
| Under 0.187 (4.75) thickness or diameter | 125 000 (860) | 115 000 (795) | 10 | -- | -- | -- | -- | -- |
| 0.187 (4.75) to under 1.75 (44.45), incl | 125 000 (860) | 115 000 (795) | 10 | -- | -- | 25 | -- | -- |
| 1.75 (44.45) to under 2.50 (63.50), incl | 120 000 (825) | 110 000 (760) | 8 | -- | -- | 20 | -- | -- |
| 2.50 (63.50) to 4.00 (101.60), incl | 120 000 (825) | 110 000 (760) | 8 | 8 | 8 | 15 | 15 | 15 |
| Bend Testing | ||||||||
| Under 0.070 (1.778) in thickness | 9 T | |||||||
| 0.070 (1.778) to 0.187(4.75), incl | 10 T | |||||||